Read 193 reviewsMilk white viscous emulsion, no mechanical impurities.1. Product DescriptionSBR latex is a stable emulsion formed by low-temperature polymerization of butadiene and styrene. Carboxy styrene butadiene rubber latex for lithium battery is a terpolymer formed by emulsion polymerization of butadiene, sty
17 people are viewing this right now
Milk white viscous emulsion, no mechanical impurities.
1. Product Description
SBR latex is a stable emulsion formed by low-temperature polymerization of butadiene and styrene. Carboxy styrene butadiene rubber latex for lithium battery is a terpolymer formed by emulsion polymerization of butadiene, styrene, unsaturated carboxylic acid, etc. It has the properties of styrene butadiene latex.
2. Application
SBR has super strong alkali resistance, good air permeability and strong adhesion after film formation; strong aging resistance, good film formation and soft film formation. It has good compatibility, an be miscible with most anionic carboxyl groups, and is completely compatible with other additives of general battery materials. It is an excellent material for the negative electrode binder of lithium batteries.3、Index:
Item | Index | Testing Value |
Appearance | Milky white liquid | Milky white liquid |
Solid content | 49-51% | 49.80% |
PH value | 6-7 | 6.5 |
Viscosity | 100-350mpa's | 176 |
Density | 1.01-1.04g/cm3 | 1.02g/cm3 |
The average particle | / | 150nm |
Peeling temperature | / | 0℃ |
4. Use Tips
(1) The recommended addition amount is 2.4-2.6% of the total drypowder amount (calculated as solid).
(2) It is recommended that the adding time is about 60 minutes after the graphite is stirred.
(3) The stirring speed is 6m/S speed, the stirring time is 40-60min,and the material temperature is 18-22℃C.